Papa:20 kila
Kūlana:GB/T 699-1999

hiʻona
ʻOi aku ka kiʻekiʻe o ka ikaika ma mua o 15 kila, ʻaʻole hiki ke kinai ʻia, ʻaʻohe huhū ʻino deformation plasticity kiʻekiʻe maʻamau no ka kulou ʻana o ka calender flanging a me ka hana hāmare, e like me ke kuʻi ʻana arc a me ke kuʻi ʻana i ka hana kuʻihao maikaʻi, ka kuʻi ʻana i ka wā liʻiliʻi ka mānoanoa, ʻano paʻa a i ʻole. ʻO ke ʻano o nā ʻāpana paʻakikī hiki ke ʻoki ʻia i ka ʻoki ʻana i ke ʻano o ka huki ʻana i ke anu a i ʻole ke kūlana annealing maʻamau i hoʻohana maʻamau i ka hana ʻana i ka ikaika ʻaʻole nui a paʻakikī kiʻekiʻe.
Aia ke kila i ke kila kalapona haʻahaʻa haʻahaʻa kiʻekiʻe, ke kila extrusion carburized paʻakikī, he haʻahaʻa haʻahaʻa ke kila, paʻakikī maikaʻi, plasticity a weldability, ikaika tensile o 355-500mpa, elongation rate o 24%
Hiki i ka Normalizing ke hoʻoikaika i ka spheroidization o ke kila, hoʻomaʻemaʻe i ka ferrite block proeutectoid nui, a hoʻomaikaʻi i ka hana ʻoki ʻana o nā blanks ma lalo o 160HBS
ʻO ke ala ʻenehana o kakilaʻO nā ʻāpana make ʻo ia: ʻo ka hoʻolei ʻana i ka hoʻoheheʻe ʻana make blank annealing machinery rough machining cold extrusion molding recrystallization annealing machinery fine machining carburizing quenching tempering grinding polishing hui.

haku mele
C: 0.17% ~ 0.24%
Aia: 0.17% ~ 0.37%
Mn: 0.35% ~ 0.65%
S: 0.035%
P: 0.035%
Cr: 0.25%
Ni: 0.25%
Cu: 0.25
waiwai mechanical
Ka ikaika uʻi B (MPa) : ≥410(42)
Ka ikaika hua S (MPa) : ≥245(25)
Elongation 5 (%) : ≥25
ʻO ka hōʻemi ʻana o nā ʻāpana wahi (%): 55 a ʻoi aku paha
Paʻakikī: ʻaʻole mālama ʻia ka wela, ≤156HB
Laʻana nui: Laʻana nui: 25mm

ʻike ʻē aʻe

ʻO ka wehewehe ʻana o ka mālama wela: normalizing, 910 ℃, hoʻoluʻu ea.

ʻO ka hana metallographic: ferrite + pearlite.
Hoʻoponopono welao ke kila 20 a me ka paakiki kinai o ke kila no.20:
Hoʻomaʻamaʻa wela o 20 kila: No ka 20 kila, hiki ke hoʻokō i ka paʻakikī paʻakikī maʻamau o 30-35HRC.
1. Ma hope o ka mīkini paʻakikī, hoʻopau ʻia ka mea hana ma ke ʻano holoʻokoʻa e ka mālama wela (920 ℃ quenched brine), a laila hana ʻia. a ma waho o ka pōʻai kaʻa, hoʻoponopono i ke ala kī.
2. Same rough machining, i loko o ka lua ili quenching a papaʻaina wale nō quenching keyway (ma muli o ka nui o ka workpiece), a hope hoʻopau.
3. ʻO ka carburizing a me ke kinai ʻana, e wili ana i ka lua i loko a me ke ala kī.
ʻO ke kahe kaʻina ka lua, ke kolu a me ka hapa nui.
● Moku'āina hoʻouna: ka hoʻounaʻana ma keʻano o ka wela wela a iʻole ka wela wela (annealing, normalizing a iʻole ka wela wela kiʻekiʻe).Inā ʻaʻole i hōʻike ʻia, e hana ʻia ka lawe ʻana me ka ʻolelapaʻau wela.